Coating compositions and textile fabrics coated therewith

ABSTRACT

A curable coating composition that exhibits improved curs and adhesion to various substrates, especially synthetic textiles used in the manufacture of air bags, and good air pressure holding performance.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of pending U.S. application Ser. No.14/245,122 filed Apr. 4, 2014, which is a Continuation of U.S.application Ser. No. 12/647,954, new U.S. Pat. No. 8,729,170, filed Dec.28, 2009, which claims priority to U.S. Provisional Application61/141,416 filed Dec. 30, 2008, the entire contents of each are herebyincorporated by reference in their entirety.

FIELD OF THE INVENTION

The present invention relates to a new curable silicone compositionhaving excellent self-adhesive properties when coated and cured on atextile fabrics.

This coating provides excellent adhesive properties to the coated fabricperformance in regards to crease flex abrasion tests and provides a goodair pressure holding performance.

Airbag fabrics using such new curable silicone composition are alsoencompassed within this invention.

BACKGROUND OF THE PRIOR ART

At the present time, many motor vehicles are equipped with anacceleration sensor that measures the decelerations of the vehicle. Whenthe reference deceleration value is exceeded, an explosive pellettriggers the combustion of an additional charge, and then that of thecombustible solid. This solid is converted into gas (for examplenitrogen) and inflates the cushion. An airbag (or inflatable cushion) isan air-filled bag made of pleated and tight-stitched polyamide fabric.For further details regarding these personal protection bags or“airbags”, reference may be made especially to reference U.S. Pat. No.6,193,847.

Historically, these bags are formed by a web of synthetic fibre, forexample polyamide, coated on at least one of its faces with a layer ofan elastomer such as polychloroprene. But the desire to decrease thefolded size of the completed airbag and the tendency of polychloropreneto degrade, with exposure to heat, and to release hazardous chemicals(the components of hydrochloric acid) has led that silicone compositionshave easily supplanted polychloroprenes in this application.

Silicone compositions have thus found an important application in thecoating of flexible—woven, knitted or nonwoven—materials used formanufacturing personal protection bags for the occupants of vehicles,also known as “airbags”.

In an effort to improve the performance of the silicone coaling, priorart US-2005137321 describes a method for improving the tearing endcombing resistance of coated fabrics for airbags by using a siliconcomposition comprising an additive consisting of a polyorganosiloxaneresin and calcium carbonate. After coating fabric supports with saidcomposition and crosslinking, the thus coated supports exhibit adherenceand resistance properties and high tearing and combing resistanceproperties.

While fabrics coated with conventional silicone compositions may besatisfactory for standard airbag applications, the airbag industry isnow required to satisfy requirements where pressurised fluids are to beretained in a fabric envelope for a relatively long period. Thisrequirement exists for example in the application of such coatings toside curtain airbags for the automotive industry. Curtain airbags arenow designed to inflate as quickly as driver- and passenger-side bags,but they must deflate very slowly to protect the occupants during rollover and side impact. The side curtains unfold to form a cushionedcurtain between passengers and some of the side of the car body, e.g.,the windows. As the intention is not merely to cushion the blow onimpact itself, as is the case for conventional driver and passengerairbags, but e.g. to protect passengers when a car is rolling, it isimportant that the side curtain air bag is sufficiently pressurisedduring such rolling process. Where conventional driver and passengerairbags only need to retain pressure for a fraction of a second, it isdesirable that side curtain airbags maintain a suitable pressure for afew seconds. Similar applications exist where a pressurised fabricstructure is desired to maintain a certain fluid pressure for arelatively extended period of time, e.g. in emergency chutes foraeroplanes, inflatable rafts etc. Thus, it is now imperative that thebag exhibits a very low leakage rate after the bag experiences peakpressure during the instantaneous quick inflation. Hence, the coating onthe bag must be performant enough to withstand the shock and stresseswhen the bag is inflated so quickly.

Silicone polymers have excellent thermal properties but have relativelyhigh permeability to gases, when compared to many other elastomers. Thishas not been a matter of concern in coatings used for conventionalairbags, since the retention time requirements are very small. Theadvent of side curtains, with higher air retention requirements isbringing to light the difficulties in achieving the desired retentionproperties at desired add-on levels.

That aside, silicone rubbers obtained from curing conventional siliconecompositions originally have poor adhesive properties and have hadproblems concerning the property of bonding or adhering to fibers. As anexpedient for this, it has been attempted to impart self-adhesiveproperties to silicone rubbers by adding a suitable additive ingredientto silicone rubber raw compositions.

For example, in prior art U.S. Pat. No. 5,296,298, example of siliconecompositions showing good adhesion on the airbag support are described.However, these compositions are not adapted to the new expectations ofairbag manufacturers as regards controlling the slipperiness propertiesof the airbag.

Furthermore, there is still a need for good adhesive properties so thatit fulfils the requirement of standard test used within the airbag fieldsuch as “The Crease Flex Testing method”. This method is employed forrepeated bending and it determines the stage of dryness and adherencereached by a material covered with silicone and used for airbags.

The present invention is directed towards overcoming the drawbacks ofthe prior art.

SUMMARY OF THE INVENTION

In this perspective, one of the important objectives of the invention isto provide a silicone coating composition that may be cured bypolyaddition or free-radical reactions, which is useful especially forapplications in the field of inflatable safety bags for vehicles, orairbags, and which has, after curing and coating on a fabric, optimumproperties in terms of pressure retention characteristics (air-holding),high resistance to sudden inflation, slipperiness, i.e. a goodcoefficient of friction, abrasion (rubbing-off), high adhesion to thesubstrate and good thermal resistance. An airbag coated with the presentsilicone coating composition is also disclosed. This coating providesexcellent adhesive properties to the coated fabric and provides a goodair pressure holding performance and good performance in regards tocrease flex abrasion tests. Airbag fabrics using such new curablesilicone composition are also encompassed within this invention.

DETAILED DESCRIPTION

According to a first aspect of the invention, there is provided acurable silicone composition (A) useful for coating textile fabrics andcomprising:

(1) components (a-1) or (a-2):

-   -   (a-1) corresponding to at least one polyorganosiloxane that may        be cured by the action of a catalyst based on at least one        organic peroxide, and    -   (a-2) corresponding to a polyorganosiloxane blend that may be        cured by polyaddition reactions, comprising;        -   at least one organopolysiloxane (I) having an average of at            least two silicon-bonded aliphatically unsaturated            hydrocarbon substituents on the molecule, and        -   at least one organopolyorganosiloxane (II) and/or at least            one organosilicon crosslinker (II′) having an average of at            least 2 and most preferably at least 3 silicon-bonded            hydrogen on the molecule,

(2) an effective amount of a curing catalyst (III) consisting: whencomponent (a-1) is used, of at least one organic peroxide, and whencomponent (a-2) is used, of at least one catalyst able to promote thereaction of the aliphatically unsaturated hydrocarbon substituents withSiH groups,

(3) at least 10 weight parts, per 100 weight parts of the curablesilicone composition, of an organopolysiloxane resin (IV) of formulaMM^(Vi)Q and consisting essentially of:

-   -   (a) monovalent siloxane units M^(Vi)Q of the formula        R′R₂SiO_(1/2);    -   (b) monovalent siloxane units M of the formula R₃SiO_(1/2), and    -   (c) tetravalent siloxane units Q of the formula SiO_(4/2),

wherein R denotes a monovalent hydrocarbon group and R′ denotes a vinylgroup:

(4) an organopolysiloxane resin (V) different, from the saidorganopolysiloxane resin (IV) and comprising at least two differentsiloxane units chosen from those of M siloxane unit of formulaR₃SiO_(1/2) D siloxane unit of formula R₂SiO_(2/2), T siloxane unit offormula RSiO_(3/2) and Q siloxane unit of formula SiO_(4/2).

wherein R denotes a monovalent hydrocarbon group, with the conditionsthat at least one of these siloxane units being a T or Q siloxane unitand that at least one of the M, D and T siloxane units comprises analkenyl group

(5) at least one adhesion promoter (VI),

(6) at least one reinforcing filler (VII),

(7) optionally at least one polydiorganosiloxane gum (XI) which is alinear or partially-branched homopolymer or copolymer having at least 2alkenyl groups per molecule and the said gum having a viscosity ofgreater than 500,000 mPa·s at 25° C.,

(8) optionally, at least one curing inhibitor (VII),

(9) optionally, at least one coloration additive (IX), and

(10) optionally, at least one additive (X) for improving the fireresistance,

It is to the Applicant's credit to have demonstrated the importance ofthe presence of specific combination of:

-   -   at least 10 weight parts, per 100 weight parts of the curable        silicone composition, of an organopolysiloxane resin (IV) of        formula MM^(VI)Q, and    -   an organopolysiloxane resin (V) different from        organopolysiloxane resin (IV) which also bears in its structure        alkenyl groups.

The presence of such specific combination within a curable siliconecoating composition provides good air pressure holding performance andgood performance in regards to crease flex abrasion tests (adhesiveproperties) of the coated fabric.

This is all the more surprising since this gain does not become lost atthe expense of the other hardness, mechanical .strength, surfaceuniformity and heat resistance properties of the silicone coating.

In a preferred embodiment of the invention, the organopolysiloxane resin(IV) is present from 15 to 50 weight parts per 100 weight parts of thecurable silicone composition and most preferably at 20 to 40 weightparts per 100 weight parts of the curable silicone composition.

In a preferred embodiment of the invention the organopolysiloxane resin(V) is added at 1 to 50 weight parts per 100 weight parts of the curablesilicone composition.

Preferably, the organopolysiloxane resin (V) is selected from the groupconsisting of:

-   -   an organopolysiloxane resin of formula MT^(Vi)Q consisting        essentially of:        -   (a) trivalent siloxane units T^(Vi) of the formula            R′SiO_(3/2);        -   (b) monovalent siloxane units M of the formula R₃SiO_(1/2),            and        -   (c) tetravalent siloxane units Q of the formula SiO_(4/2)    -   an organopolysiloxane resin of formula MD^(Vi)Q consisting        essentially of:        -   (a) divalent siloxane units D^(Vi) of the formula            RR′SiO_(2/2);        -   (b) monovalent siloxane units M of the formula R₃SiO_(1/2),            and        -   (c) tetravalent siloxane units Q of the formula SiO_(4/2)    -   an organopolysiloxane resin of formula MDD^(Vi)Q consisting        essentially of:        -   (a) divalent siloxane units D^(Vi) of the formula            RR′SiO_(2/2):        -   (b) divalent siloxane units D of the formula R₂SiO_(2/2)        -   (b) monovalent siloxane units M of the formula R₃SiO_(1/2),            and        -   (c) tetravalent siloxane units Q of the formula SiO_(4/2)    -   an organopolysiloxane resin of formula M^(Vi)Q consisting        essentially of:        -   (a) monovalent siloxane units M^(Vi) of the formula            R′R₂SiO_(1/2); and        -   (b) tetravalent siloxane units Q of the formula SiO_(4/2),            and    -   an organopolysiloxane resin of formula M^(Vi)T^(Vi)Q consisting        essentially of:        -   (a) monovalent siloxane units M^(Vi) of the formula            R′R₂SiO_(1/2);        -   (b) trivalent siloxane units T^(Vi) of the formula            R′SiO_(3/2) and        -   (c) tetravalent siloxane units Q of the formula SiO_(4/2)            wherein R denotes a monovalent hydrocarbon group and R′            denotes a vinyl group:

The most preferred organopolysiloxane resin (V) is an organopolysiloxaneresin of formula MD^(Vi)Q consisting essentially of:

-   -   (a) divalent siloxane units D^(Vi) of the formula RR′SiO_(2/2);    -   (b) monovalent siloxane units M of the formula R₃SiO_(1/2), and    -   (c) tetravalent siloxane units Q of the formula SiO_(4/2)        wherein R denotes a monovalent hydrocarbon group and R′ denotes        a vinyl group:

The polyorganosiloxane (a-1) that is curable by the action of a catalystbased on at least one organic peroxide is advantageously a productcontaining siloxyl units of formula:

$\begin{matrix}{R_{a}^{1}{SiO}\frac{( {4 - a} )}{2}} & ( {I\text{-}1} )\end{matrix}$

in which:

-   -   the symbols R¹, which may be identical or different, represent a        hydrocarbon-based group containing from 1 to 12 carbon atoms and        preferably from 1 to 8 carbon atoms, which is optionally        substituted, and    -   a is 1, 2 or 3.

Preferably, the symbols R¹ are chosen from:

-   -   methyl, ethyl, propyl, butyl, hexyl and dodecyl groups,    -   cycloalkyl groups, for instance cyclohexyl,    -   alkenyl groups, for instance vinyl, allyl, butenyl and hexenyl        groups,    -   aryl groups, for instance phenyl, tolyl and aralkyl groups such        as β-phenylpropyl, and    -   the groups mentioned above in which one or more hydrogen atoms        are replaced with one or more halogen atom, a cyano group or a        cyano group equivalent, for instance a chloromethyl,        trifluoropropyl or cyanoethyl.

Even more preferentially, the polyorganosiloxanes (a-1) are terminatedat the chain ends with trimethylsilyl, dimethylvinyl,dimethylhydroxysilyl or trivinylsilyl units.

In one particularly advantageous embodiment, the polyorganosiloxanes(a-1) contain at least two alkenyl groups per molecule.

Among the organic peroxides that may be used with component (a-1)according to the invention, mention may be made of benzoyl peroxide,bis(p-chlorobenzoyl) peroxide, bis(2,4-dichlorobenzoyl) peroxide,dicumyl peroxide, di-t-butyl peroxide,2,5-dimethyl-2,5-di(t-butylperoxy)hexane, t-butyl perbenzoate,t-butylcumyl peroxide, halogenated derivatives of the peroxidesmentioned above, for instance bis(2,4-dichlorobenzoyl) peroxide,1,6-bis(p-toluoylperoxycarbonyloxy)hexane,1,6-bis(benzoylperoxycarbonyloxy)hexane,1,6-bis(p-toluoyl-peroxycarbonyloxy)butane and1,6-bis(2,4-dimethylbenzoylperpoxycarbonyloxy)hexane.

The polyorganosiloxane (I) of the silicone coating composition (A) usedfor the mode of curing by means of polyaddition reactions comprises:

(i) siloxyl units of formula (I-1):

$\begin{matrix}{R_{a}^{1}Z_{b}{SiO}\frac{4 - ( {a + b} )}{2}} & ( {I\text{-}1} )\end{matrix}$

in which:

-   -   the symbols R¹ represent an alkenyl group, preferably a vinyl or        allyl group,    -   the symbols Z, which may be identical or different, each        represent a monovalent hydrocarbon-based group, free of        unfavourable action on the activity of the catalyst and chosen        from alkyl groups containing from 1 to 8 carbon atoms inclusive,        optionally substituted with at least one halogen atom, and also        from aryl groups,    -   a is 1 or 2, b is 0, 1 or 2 and the sum a+b is equal to 1, 2 or        3, and optionally        (ii) other siloxyl units of formula (I-2):

$\begin{matrix}{{Zc}\mspace{11mu} {SiO}\frac{4 - c}{2}} & ( {I\text{-}2} )\end{matrix}$

in which:

-   -   Z has the same meaning as above and c is 0, 1, 2 or 3.

This polydiorganosilioxane (I) may have a viscosity at least equal to100 mPa·s and preferably less than 200,000 mPa·s.

All the viscosities concerned in the present specification correspond toa dynamic viscosity magnitude that is measured, in a manner that isknown per se, at 25° C.

The polyorganosiloxane (I) may be formed solely from units of formula(I-1) or may contain, in addition, units of formula (I-2). Similarly, itmay have a linear, branched, cyclic or network structure. Z is generallychosen from methyl, ethyl and phenyl radicals, 80 mol % (or in numericalterms) at least of the radicals Z being methyl radicals.

Examples of siloxyl units of formula (I-1) are vinyldimethylsiloxyl,vinylphenylmethylsiloxyl, vinylmethylsiloxyl and vinylsiloxyl units.

Examples of polyorganosiloxanes (I) are linear and cyclic compounds, forinstance; dimethylpolysiloxanes containing dimethylvinylsilyl endgroups, (methylvinyl)(dimethyl)polysiloxane copolymers containingtrimethylsilyl end groups, (methylvinyl)(dimethyl)polysiloxanecopolymers containing dimethylvinylsilyl end groups and cyclicmethylvinylpolysiloxanes.

Advantageously, the polyorganosiloxane (II) comprises siloxyl units offormula (II-1):

$\begin{matrix}{H_{d}L_{e}{SiO}\frac{4 - ( {d + e} )}{2}} & ( {{II}\text{-}1} )\end{matrix}$

in which:

-   -   the groups L, which may be identical or different, each        represent a monovalent hydrocarbon-based group, free of        unfavourable action on the activity of the catalyst and chosen,        preferably, from an alkyl group containing from 1 to 8 carbon        atoms inclusive, optionally substituted with at least one        halogen atom, advantageously from methyl, ethyl, propyl and        3,3,3-trifluoropropyl groups, and aryl groups, and        advantageously a xylyl, tolyl or phenyl radical,    -   d is 1 or 2, e is 0, 1 or 2, the sum d+e is equal to 1, 2 or 3,        and    -   optionally, at least some of the other units being units of mean        formula:

$\begin{matrix}{L_{g}{SiO}\frac{4 - g}{2}} & ( {{II}\text{-}2} )\end{matrix}$

in which the groups L have the same meaning as above and g is equal to0, 1,2 or 3.

The dynamic viscosity of this polyorganosiloxane (II) is at least equalto 10 mPa·s and preferably between 20 and 1000 mPa·s.

The polyorganosiloxane (II) may be formed solely from units of formula(II-1) or may also comprise units of formula (II-2). Thepolyorganosiloxane (II) may have a linear, branched, cyclic or networkstructure. The group L has the same meaning as the group Z above.Examples of units of formula (II-1) are: H(CH₃)₂SiO_(1/2), HCH₃SiO_(2/2)and H(C₆H₅)SiO_(2/2).

The examples of units of formula (II-2) are the same as those givenabove for the units of formula (I-2).

Examples of polyorganosiloxanes (II) are linear and cyclic compounds,for instance:

-   -   dimethylpolysiloxanes containing hydrogenodimethylsilyl end        groups,    -   copolymers containing (dimethyl) (hydrogenomethyl)polysiloxane        units containing trimethylsilyl end groups,    -   copolymers containing (dimethyl)(hydrogenomethyl)polysiloxane        units containing hydrogenodimethylsilyl end groups,    -   hydrogenomethylpolysiloxanes containing trimethylsilyl end        groups,    -   cyclic hydrogenomethylpolysiloxanes.

The compound (II) may optionally be a mixture of a dimethylpolysiloxanecontaining hydrogenodimethylsilyl end groups and of a polyorganosiloxanecomprising at least three hydrogenosiloxyl group.

The ratio of the number of hydrogen atoms linked to silicon in thepolyorganosiloxane (II) and in the crosslinker (II′) to the total numberof groups containing alkenyl unsaturation of the polyorganosiloxane (I)is between 0.4 and 10, preferably between 0.6 and 5 and most preferablybetween 1.5 to 2.5.

According to one particular embodiment, the following are used:

at least one linear polyorganosiloxane (I) comprising chains formed fromunits of formula (I-2) in which c=2, blocked at each of their ends withunits of formula (I-1) in which a=1 and b=2, and

at least one linear polyorganosiloxane (II) comprising in its structureat least three hydrogen atoms linked to silicon, located in the chainsand/or at chain ends.

According to another particular embodiment, the following are used:

-   -   at least one linear polyorganosiloxane (I) comprising chains        formed from units of formula (I-2) in which c=2, blocked at each        of their ends with units of formula (I-1) in which a=1 and b=2,        and    -   at least one linear polyorganosiloxane (I) comprising chains        formed from units of formula (II-1) in which d=1 and e=1 and        optionally units of formula (II-2) in which g=2, blocked at each        of their ends with units of formula (II-1) in which d=1 and e=2.

Organosilicon crosslinker (II′) for use in the curable silicone coatingcomposition according to the invention are preferably selected fromsilanes, low molecular weight organosilicon resins and short chainorganosiloxane polymers. Organosilicon crosslinker (II′) compound has atleast 3 silicon-bonded hydrogens which are capable of reacting with thesilicon-bonded aliphatically usaturatred hydrocarbon substituent ofpolyorganosiloxane (I) by addition reaction between the crosslinkingorganosilicon compound and the organopolysiloxane.

A suitable silane which may serve as organosilicon crosslinker (II′)compound is methyltrihydrogenosilane. Suitable organosilicon resincompounds include organosilicon resins consisting mainly oftetrafunctional siloxane units of the formula SiO_(4/2) andmonofunctional units R_(y)H_(w)SiO_(1/2), wherein R is a monovalenthydrocarbon group having up to 18 carbon atoms, v and w each have avalue of from 0 to 3, the sum of v+w being 3. Suitable short chainorganosiloxane polymers include those having at least 3 silicon-bondedhydrogen atoms per molecule and may be linear or cyclic. Preferredorganosilicon crosslinkers have the general formula:

wherein R⁴ denotes an alkyl or aryl group having up to 10 carbon atoms,R³ is a group R⁴ or a hydrogen atom, p has a value of from 0 to 20, qhas a value of from 1 to 70, and there are at least 3 silicon-bondedhydrogen atoms present per molecule. It is not crucial but preferredthat the silicon-bonded hydrogen atoms are on terminal silicon atoms forlinear siloxane compounds. It is preferred that R⁴ denotes a lower alkylgroup having no more than 3 carbon atoms, most preferably a methylgroup. R³ preferably denotes an R⁴ group. Preferably p=0 and q has avalue of from 2 to 70, more preferably 2 to 30, or where cyclicorganosilicon materials are used, from 3 to 8. It is most preferred thatthe organosilicon crosslinker is a siloxane polymer having a viscosityof from 1 to 150 mm ²/s at 25° C., more preferably 2 to 100 mm ²s, mostpreferably 5to 80 mm ²/s. The cross-linking organosilicon compound maycomprise a mixture of several materials as described.

Examples of suitable organosilicon crosslinkers are trimethylsiloxaneend-blocked polymethylhydrogenosiloxane having up to for example 20carbon atoms, dimethylhydrogenosiloxane end-blocked methylhydrogenosiloxane, dimethylsiloxane methylhydrogenosiloxane copolymer andtetramethylcyclotetrasiloxane.

The size of the organosilicon crosslinker is not crucial, but preferredare short chain organosiloxane polymers having at least threesilicon-bonded hydrogen atoms, which have a chain length of from 2 to 50silicon atoms, more preferably from 5 to 20.

The curing catalyst (III) when component (a-2) is used consists of atleast one metal (or compound) of the platinum group, which are also wellknown. The metals of the platinum group are those known under the nameplatinoids, this term combining, besides platinum, ruthenium, rhodium,palladium, osmium and iridium. Platinum and rhodium compounds arepreferably used. Complexes of platinum and of an organic productdescribed in patents U.S. Pat. No. 3,159,601, U.S. Pat. No. 3,159,602,U.S. Pat. No. 3,220,972 and European patents EP-A-0 057 459, EP-A-0 188978 and EP-A-0 190 530, and complexes of platinum and ofvinylorganosiloxanes described in patents U.S. Pat. No. 3,419,593, U.S.Pat. No. 3,715,334, U.S. Pat. No. 3,377,432 and U.S. Pat. No. 3,814,730may be used in particular. The catalyst that is generally preferred isplatinum. In this case, the weight amount of catalyst (III), calculatedby weight of platinum metal, is generally between 2 and 400 ppm,preferably between 5 and 200 ppm on the basis of the total weight of thepolyorganosiloxanes (I) and (II).

Without this being limiting, it may be considered that the adhesionpromoter (VI) includes epoxy-functional, organotitanates oramino-functional organosilicon.

In a prefered embodiment the adhesion promoter (VI) compound is amixture of:

-   -   (VI.1) at least one alkoxy organosilane containing, per        molecule, at least one ₂-C₆ alkenyl group,    -   (VI.2) at last one organosilicon compound comprising at least        one epoxy radical, and    -   (VI.3) at least one metal chelate M and/or a metal alkoxide of        general formula:

M(OJ)n

With:

-   -   M being chosen from the group formed by: Ti, Zr, Ge, Li, Mn, Fe,        Al and Mg, and    -   n=valency of M and J=linear or branched C₁-C₈ alkyl.

According to the invention, an advantageous combination for the adhesionpromoter is as follows:

-   -   vinyltrimethoxysilane (VTMO), representative of formula (VI.1).    -   3-glycidoxypropyltrimethoxysilane (GLYMO), representative of        formula (VI.2), and    -   butyltitanate, representative of formula (VI.3).

Advantageously, the adhesion promoter (VI) is present in a proportion offrom 0.1% to 10%, preferably 0.5% to 5% and even more preferably 0.5% to3% by weight relative to all of the constituents of the curable siliconecomposition (A).

Examples of suitable reinforcing filler (VII), may include silica, e.g.turned silica, precipitated silica, gel-formation silica, aerosils,titania, standard calcium carbonate or calcium carbonate that hasundergone a compatibilization treatment.

The filler may have a hydrophobic surface, which may be obtained bytreating the filler e.g. With suitable silanes, short chain siloxanes,fatty acids or resinous silicone materials. Suitable materials andprocesses for rendering the surface of fillers hydrophobic have beendescribed in the literature, and are known to the person skilled in theart. The amount of reinforcing filler is again not crucial, butpreferably from 5 to 50% by weight of the total curable siliconecomposition (A) consists of the filler, more preferably from 5 to 40%and most preferably 10 to 30%.

The curable silicone composition (A) according to the invention may alsocomprise a standard semi-reinforcing or packing filler, for examplediatomaceous earth or ground quartz.

Other non-siliceous minerals may be included as semi-reinforcing orpacking mineral fillers: carbon black, titanium dioxide, aluminiumoxide, hydrated alumina, expanded vermiculite, non-expanded vermiculite,zinc oxide, mica, talc, iron oxide, barium sulfate, slaked lime, etc.

These non-siliceous minerals fillers may also be present in a proportionof from 5% to 40% by weight and preferably from 5% to 30% relative tothe total weight composition.

The polydiorganosiloxane gum (XI) is a polyorganosiloxane whichpreferably has an average unit formula R_(a)SiO_(4-a)/2) (with a=1, 2 or3) which may have a linear or partially-branched structure but ispreferably linear. Each R may be the same or different. With the provisothat the polyorganosiloxane has at least two alkenyl groups permolecule, R is a substituted or non-substituted monovalent hydrocarbongroup which may be for example an alky; group, such as a methyl, ethyl,propyl, butyl, and octyl groups; aryl groups such as phenyl and tolylgroups; aralkyl groups; alkenyl groups for example, vinyl, allyl,butenyl, hexenyl, and heptenyl groups; and halogenated alkyl groups forexample chloropropyl and 3,3,3-trifluoropropyl groups.

The polydiorganosiloxane gum (XI) may be-terminated by any of the abovegroups. When R is an alkenyl group the alkenyl group is preferably vinylgroup or hexenyl group. Indeed the alkenyl groups may be on terminalgroups and/or polymer side chains.

Examples of the polydiorganosiloxane gum (XI) are:dimethylvinylsiloxy-terminated polydimethylsiloxane,trimethylsiloxy-terminated polydimethylsiloxane,trimethylsiloxy-terminated copolymer of methylvinylsiloxane anddimethylsiloxane, dimethylvinylsiloxy-terminated copolymer ofmethylvinylsiloxane, dimethylhexenylsiloxy-terminatedpolydimethylsiloxane, trimethylsiloxy-terminated copolymer ofmethylhexenylsiloxane and dimethylsiloxane,dimethylhexenylsiloxy-terminated copolymer of methylhexenylsiloxane anddimethylsiloxane, dimethylvinylsiloxy-terminated copolymer ofmethylphenylsiloxane and dimethylsiloxane,dimethylhexenylsiloxy-terminated copolymer of methylphenylsiloxane anddimethylsiloxane, dimethylvinylsiloxy-terminated copolymer ofmethyl(3,3,3-trifluoropropyl)siloxane and dimethylsiloxane, anddimethylhexenylsiloxy-terminated copolymer ofmethyl(3,3,3-trifluoropropyl)siloxane and dimethylsiloxane.

Such polydiorganosiloxane gum (XI) are for example described in patentsU.S. Pat. Nos. 3,142,655, 3,821,140, 3,836,488 and 3,839,266). Thesegums advantageously have a viscosity at 25° C. of at least equal to 0.5million mPa·s and preferably of between 1 million to 10 million mPa·s.

In a prefered embodiment of the invention, the polydiorganosiloxane gum(XI) is added at 1 to 40 parts by weight per 100 weight parts of thecurable silicone composition.

The curing inhibitor (VIII) may be chosen from the following compounds:

-   -   acetylenic alcohols.    -   polyorganosiloxanes substituted with at least one alkenyl that        may optionally be in cyclic form, tetramethylvinyltetrasiloxane        being particularly preferred,    -   pyridine,    -   organic phosphines and phosphites,    -   unsaturated amides, and    -   alkyl maleates.

These acetylenic alcohols (Cf. FR-B-1 528 464 and FR-A-2 372 874), whichare among the preferred hydrosilylation-reaction thermal blockers, havethe formula:

(R′)(R″)(OH)C═C≡CH

in which:

-   -   R′ is a linear or branched alkyl radical, or a phenyl radical;        and    -   R″ is H or a linear or branched alkyl radical, or a phenyl        radical; the radicals R′ and R″ and the carbon atom α to the        triple bond possibly forming a ring.

The total number of carbon atoms contained in R′ and R″ being at least 5and preferably from 9 to 20.

For the said acetylenic alcohols, examples that may be mentionedInclude:

-   -   1-ethynyl-1-cyclohexanol;    -   3-methyl-1-dodecyn-3-ol;    -   3,7,11trimethyl-1-dodecyn-3-ol;    -   1,1-diphenyl-2-propyn-1-ol;    -   3-ethyl-6-ethyl-nonyn-3-ol;    -   2-methyl-3-butyn-2-ol;    -   3-methyl-1-pentadecyn-3-ol; and    -   diallyl maleate or diallyl maleate derivatives.

These α-acetylenic alcohols are commercial products. Such curinginhibitor (VIII) is present in a proportion of up to 1 part by weightrelative to the total amount of the composition (A).

Other additional components may be included in suitableelastomer-forming compositions, including other fillers, chainextenders, dyes, colorants, pigments, viscosity modifiers, bath-lifeextenders, curing inhibitors (VIII), coloration additive (IX) andflexibilisers.

As additive (IX) for improving the fire resistance, examples that may bementioned include compounds containing a phenyl group substituted withan amino (secondary or tertiary) group. Examples of such additives arefound in the reference U.S. Pat. No. 5,516,938. The useful amounts ofsuch additives are generally between 0.01 and 1 part by weight relativeto the total amount of the composition.

In a manner that is known per se, the curable silicone composition (A)according to the invention may be supplemented with various conventionaladditives, for instance dyes.

The curable silicone composition (A) may be prepared by merely mixingthe ingredients in the desired ratios. However, for reasons of storagestability and bath life before or during application of the compositionsto the textile fabric, it is preferred to store the composition in twoparts A and B, by separating the curing catalyst (III) from theorganosilicon crosslinker (II′) or polyorganosiloxanes (II) which bearhydrogeno substituents. The other components of the compositions areoften distributed over both parts in proportions which will allow easymixing of the two parts immediately prior to application. Such easymixing ratios may be e.g. 1/10 or 1/1 ratios.

Once mixed together, the parts A and B form a ready-to-use siliconecomposition, which may be applied to the support by any suitable coatingmeans (for example by doctor blade or roll).

The invention is also directed towards a method of coating a synthetictextile comprising applying the curable silicone composition (A) asdescribed above to a synthetic textile, and allowing the coatingcomposition to cure.

In a prefered embodiment, the synthetic textile is an airbag fabric.

The curable coating compositions (A) may be applied according to knowntechniques to the textile fabric substrates. These include spraying,gravure coating, bar coating, coating by knife-over-roller, coating byknife-over-air, padding and screen-printing. It is preferred that thecomposition is applied by a knife-over-air or knife-over-roller coatingmethod. It is also preferred that the composition is applied to acoat-weight prior to curing of at least 20 -g/m². Preferably the coatingthickness is from 25 to 150 g/m², more preferably from 25 to 50 g/m² andeven more preferably from 30 to 35 g/m² or applications where pressureneeds to be maintained longer, e.g. in side curtain airbags, or 3.0 to50 g/m² for applications where the pressure retention is not so criticalover prolonged periods, e.g. in standard driver airbags. In order tomake the compositions easily applicable to the textile fabric, it ispreferred that the viscosity of the composition (A) is from 10,000 to30000 mPa·s. The textile fabric is preferably scoured prior toapplication, in order to ensure good adhesion of the composition.

Although it is not preferred, it is possible to apply the composition inmultiple layers, which together fulfill the preferred criteria set outabove. It is also possible to apply onto the coating composition afurther coating, e.g. of a material providing low friction, or anadditional textile fabric, whether woven or non-woven to improve thestrength and/or the feel of the fabric.

The compositions according to the invention are heat-cured and/or curedby electromagnetic radiation (radiation of accelerated electrons or“electron beam”). The compositions according to the invention- may beused for covering or coating flexible supports, especially woven,knitted or nonwoven fibrous textiles, and preferably woven, knitted ornonwoven supports made of synthetic fibres, advantageously of polyesteror polyamide.

Curing conditions for the coating are preferably at elevatedtemperatures over a period which will very depending on the actualtemperature used, for example 120 to 200° C. for a period of up to 5minutes.

The advantage of the Invention is that without having to combinemultiple layers of coating on the surface of a textile fabric the fabricis still very able to form a barrier between areas of differingpressure. Particularly useful applications for textile fabrics coatedaccording to the present invention are those applications where thefabric is formed into art envelope and pressure is applied inside theenvelope, e.g. by introducing gas into the envelope and thus inflatingit. Particularly useful applications include automotive airbags,emergency shoots on aeroplanes, hot air balloons. The most valuable useof fabrics according to the invention is in the production of sidecurtain airbags for automobiles; where the internal pressure of theenvelope needs to be maintained for a relatively long period of time,e.g. from 1 to 5 seconds.

A final deposited thickness after curing of between 25 and 300 μm andespecially between 50 and 200 μm will generally be targeted. It is notnecessary to have a uniform thickness, since, if the surface of thesupport is not regular, it may result in an irregular deposition.

Another aspect of the invention concerns a textile fabric coated on oneor two faces with a cured coating composition obtained by curing thecurable silicone coating composition (A) as described above.

The invention also concerns an airbag fabric coated on one or two faceswith a cured coating composition obtained by curing the curable siliconecoating composition (A) as described above.

Finally, the Invention concerns an inflatable bag comprising an airbagfabric coated according to the process described above.

The examples that follow, of the preparation of compositions and oftheir application as coating for polyamide fabric according to theprocess of the invention, will allow the invention to be understood moreclearly and will allow its advantages and implementation variants to behighlighted. The performance qualities of the products resulting fromthe process according to the invention will be illustrated by means ofcomparative tests. All parts and percentages are by weight unlessotherwise stated, and values of viscosity in these examples are measuredusing a Brookfieid viscometer according to the indications of AFNORstandard NFT-76-106 of May 1982relate to dynamic viscosity at 25° C.

EXAMPLES

5 compositions described in Tables 1 and 2 were prepared by mixing in a1:1 weight ratio of part A and B. The compositions were applied to asynthetic textile and allow to cure by thee application of heal. Thecoated synthetic textile was then tested for adhesion of the compositionto the synthetic textile by a Crease Flex Test that determines thenumber of Crease Flex Cycles. The Crease Flex Test protocol and the Testresults are shown in Table 3.

Grease Flex Test Protocol & Results

The method is employed for repeated bending and it determines the stageof dryness and adherence reached by a material covered with silicone andused for airbags.

The test protocol for measuring the Crease Flex in Cycles to Failure ofthe coated synthetic textiles prepared above, was carried out using aScoff No. 383 Type Folding and Abrasion Tester sold by Test Machines,Incorporated, Ronkonkoma, N.Y., and manufactured by Toyo SeskiSeisaku-Sho, Ltd., Tokyo, Japan. This test is widely used in theindustry for measuring the fold abrasion and the resistance against foldfatigue, of synthetic textiles, rubber, and cloth. According to thestandard test protocol, two coated fabric test strips of measuring 25millimeter×120 millimeter are placed together, with the coated sidesfacing each other. The reciprocating distance of folding is set for 6centimeter. The test strips are placed in test clamps, and the appliedpressure is adjusted to 1 Kilogram. The test measures the number ofcycles of folding. The number of cycles are counted to the failure pointof lost adhesion of coating composition applied to the Nylon fabric.

TABLE 1 Ex. 1 Ex. 2 Comparative Comparative Part by Part by Componentsweight weight Description Part (I.1) 0.00 16.95α,ω-vinyldimethylsiloxane end- A blocked polydimethylsiloxane having aviscosity of about 10 000 mPa · s (I.2) 16.00 16.95α,ω-vinyldimethylsiloxane end- blocked polydimethylsiloxane having aviscosity of about 60 000 mPa · s (II) 12.76 13.20 α,ω-trimethylsiloxaneend-blocked poly(dimethyl)(hydrogenomethyl) siloxane having a viscosityof 25 mPa · s (VII) 6.00 6.00 Calcium carbonate, CaCO₃ (Albacar ® 5970).(IV) 0.00 36.70 Polyorganosiloxane resin of formula MM^(Vi)Q (V) 55.000.00 Polyorganosiloxane resin of formula MM^(Vi)Q (XI) 5.24 5.24 Gum:α,ω-trimethylsiloxane end- blocked poly(dimethyl)(methylvinyl)-siloxane, having a viscosity of 20 million mPa · s (VI.1)2.50 2.50 Vinyltrimethoxysilane (VTMO), (VI.2) 2.50 2.50Glycidoxypropyltrimethoxysilane (GLYMO) (VIII) 0.02 0.02Ethynylcyclohexanol 1 Part (IV) 0.00 39.70 Polyorganosiloxane resin offormula B MM^(Vi)Q (V) 59.50 0.00 Polyorganosiloxane resin of formulaMM^(Vi)Q (I.1) 0.00 26.40 α,ω-vinyldimethylsiloxane end- blockedpolydimethylsiloxane having a viscosity of about 10 000 mPa · s (I.2)32.95 26.40 α,ω-vinyldimethylsiloxane end- blocked polydimethylsiloxanehaving a viscosity of about 60 000 mPa · s (VII) 6.00 6.00 Calciumcarbonate, CaCO₃ (Albacar ® 5970). (VI.3) 1.50 1.50 Butyl titanateTi(OBu)4 (TBT); (III) 0.05 0.05 Pt complex 1.70 1.70 Ratio SiH/Si(vinyl)

Ex. 3 Ex. 4 Ex. 5 Comparative Invention Invention Percent by Percent byPercent by Components weight weight weight Description Part (I) 54.161.16 4.36 α,ω-vinyldimethylsiloxane end- A blocked polydimethylsiloxanehaving a viscosity of about 10 000 mPa · s (II) 12.50 17.60 14.30α,ω-trimethylsiloxane end-blocked poly(dimethyl)(hydrogenomethyl)siloxane having a viscosity of 25 mPa · s (VII) 12 12 12 Calciumcarbonate, CaCO₃ (Albacar ® 5970). (IV) 10 58 58 Polyorganosiloxaneresin of formula MM^(Vi)Q (XI) 5.24 5.24 5.24 Gum: α,ω-trimethylsiloxaneend- blocked poly(dimethyl) (methylvinyl)-siloxane, having a viscosityof 20 million mPa · s (VI.1) 3.00 3.00 3.00 Vinyltrimethoxysilane(VTMO), (VI.2) 3.00 3.00 3.00 Glycidoxypropyltrimethoxysilane (GLYMO)(VIII) 0.10 0.10 0.10 Ethynylcyclohexanol 1 Part (V) 58.00 58.00 10.00Polyorganosiloxane resin of formula B MM^(Vi)Q (I) 28.45 28.45 76.45α,ω-vinyldimethylsiloxane end- blocked polydimethylsiloxane having aviscosity of about 10 000 mPa · s (VII) 12 12 12 Calcium carbonate,CaCO₃ (Albacar ® 5970). (VI.3) 1.50 1.50 1.50 Butyl titanate Ti(OBu)4(TBT); (III) 0.05 0.05 0.05 Pt complex 1.92 1.92 1.92 RatioSiH/Si(vinyl)

TABLE 3 RESULTS Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Compar- Compar- Compar-Inven- Inven- ative ative ative tion tion Crease Warp 500 1500 500 10001000 Flex direc- Abra- tion sion (cycles) Fill 500 2000 500 1000 2000direc- tion (cycles) Air Pressure −18 −30 −29 −22 −23 Holding loss in %after 5 s

Example 1=comparative, only one resin of type (V) MD^(Vi)Q is used.

Example 2=comparative, only one resin (IV) MMviQ is used.

Example 3=comparative although both resins are used, resin (IV) offormula MMviQ is used in an amount of only 5 parts by weight per 100parts of the curable composition=mixture of 1:1 by weight of parts A:and B.

Examples, 4 and 5=Invention, blend of two resins (IV) over 10 and (V),show that a silicone composition, involving a blend of 2 resinsaccording to the invention, when coated and cured onto a fabric, bringsa very good compromise between the crease flex abrasion and air holdingperformances.

Other variations may be made in compounds, compositions, and methodsdescribed without departing from the essential features of theinvention. The embodiments of the invention specifically illustratedherein are exemplary only and not Intended as limitations on their scopeexcept as defined in the appended claims.

1. A curable silicone composition (A) useful for coating textile fabricsand comprising: (1) components (a-1) or (a-2): (a-1) corresponding to atleast one polyorganosiloxane that may be cured by the action of acatalyst based on at least one organic peroxide, and (a-2) correspondingto a polyorganosiloxane blend that may be cured by a polyadditionreaction, comprising: at least one organopolysiloxane (I) having anaverage of at least two silicon-bonded aliphatically unsaturatedhydrocarbon substituents on the molecule, and at least oneorganopolyorganosiloxane (II) and/or at least one organosiliconcrosslinker (II′) having an average of at least 2 silicon-bondedhydrogen on the molecule, (2) an effective amount of a curing catalyst(III) comprising: when component (a-1) is used, at least one organicperoxide, and when component (a-2) is used, at least one catalyst ableto promote reaction of aliphatically unsaturated hydrocarbonsubstituents with SiH groups, (3) at least 10 weight parts, per 100weight parts of the curable silicone composition, of anorganopolysiloxane resin (IV) of formula MM^(Vi)Q and consistingessentially of: (a) monovalent siloxane units M^(Vi) of the formulaR′R₂SiO_(1/2); (b) monovalent siloxane units M of the formulaR₃SiO_(1/2), and (c) tetravalent siloxane units Q of the formulaSiO_(4/2) wherein R denotes a monovalent hydrocarbon group and R*′denotes a vinyl group: (4) an organopolysiloxane resin (V) differentfrom said organopolysiloxane resin (IV) and comprising at least twodifferent siloxane units chosen from those of M siloxane unit of formulaR₃SiO_(1/2), D siloxane unit of formula R₂SiO_(2/2). T siloxane unit offormula RSiO_(3/2) and Q siloxane unit of formula SiO_(4/2), wherein Rdenotes a monovalent .hydrocarbon group, on condition that, at least onesiloxane unit being a T or Q siloxane unit and that at least one of theM, D and T siloxane units comprises an alkenyl group (5) at least oneadhesion promoter (VI), (6) at least one reinforcing filler (VII), p1(7) optionally at least-one polydiorganosiloxane gum (XI) which is alinear or partially-branched homopolymer or copolymer having at least 2alkenyl groups per molecule and said gum having a viscosity of greaterthan 500,000 mPa·s at 25° C., (8) optionally, at least one curinginhibitor (VIII), (9) optionally, at least one coloration additive (IX),and (10) optionally, at least one additive (X) for improving the fireresistance.
 2. A curable silicone composition (A) according to claim 1,wherein the organopolysiloxane resin (V) is selected from the groupconsisting of: an organopolysiloxane resin of formula MT^(Vi)Qconsisting essentially of: (a) trivalent siloxane units T^(Vi) of theformula R′SiO_(3/2); (b) monovalent siloxane units M of the formulaR₃SiO_(1/2), and (c) tetravalent siloxane units Q of the formulaSiO_(4/2) an organopolysiloxane resin of formula MD^(Vi)Q consistingessentially of: (a) divalent siloxane units D^(Vi) of the formulaRR′SiO_(2/2); (b) monovalent siloxane units M of the formulaR₃SiO_(1/2), and (c) tetravalent siloxane units Q of the formulaSiO_(4/2) an organopolysiloxane resin of formula MDD^(Vi) Q consistingessentially of: (a) divalent siloxane units D^(Vi) of the formulaRR′SiO_(2/2); (b) divalent siloxane units D of the formula R₂SiO_(2/2)(b) monovalent siloxane units M of the formula R₃SiO_(1/2), and (c)tetravalent siloxane units Q of the formula SiO_(4/2) anorganopolysiloxane resin of formula M^(Vi)Q consisting essentially of:(a) monovalent siloxane units M^(Vi) of the formula R′R₂SiO_(1/2); and(b) tetravalent siloxane units Q of the formula SiO_(4/2) anorganopolysiloxane resin of formula M^(Vi)T^(Vi)Q consisting essentiallyof: (a) monovalent siloxane units M^(Vi) of the formula R′R₂SiO_(1/2);(b) trivalent siloxane units T^(Vi) of the formula R′R₂SiO_(1/2); and(c) tetravalent siloxane units Q of the formula SiO_(4/2) wherein Rdenotes a monovalent hydrocarbon group and R′ denotes a vinyl group: 3.A curable silicone composition (A) according to claim 1, wherein theorganopolysiloxane resin (V) is an organopolysiloxane resin of formulaMD^(Vi)Q consisting essentially of: (a) divalent siloxane units D^(Vi)of the formula RR′SiO_(2/2); (b) monovalent siloxane units M of theformula R₃SiO_(1/2), and (c) tetravalent siloxane units Q of the formulaSiO_(4/2) wherein R denotes a monovalent hydrocarbon group and R′denotes a vinyl group:
 4. A curable silicone composition (A) accordingto claim 1 wherein the organopolysiloxane resin (IV) is added at 15 to50 weight parts per 100 weight parts of the curable siliconecomposition.
 5. A curable silicone composition (A) according to claim 1wherein the organopolysiloxane resin (V) is added at 1 to 50 weightparts per 100 weight parts of the curable silicone composition.
 6. Acurable silicone composition (A) according to claim 1 wherein thepolydiorganosiloxane gum (XI) is added at 1 to 40 parts by weight per100 weight parts of the curable silicone composition.
 7. A method ofcoating a synthetic textile comprising applying the curable siliconecomposition (A) according to claim 1 to a synthetic textile, andallowing the coating composition to cure.
 8. A method according to claim7 in which the synthetic textile is an airbag fabric.
 9. A textilefabric coated on one or two feces with a cured coating compositionobtained by curing the curable silicone coating composition (A)according to claim
 1. 10. An airbag fabric coated on one or two faceswith a cured coating composition obtained by curing the curable siliconecoating composition (A) according to claim
 1. 11. Inflatable bagcomprising an airbag fabric coated according to claim 9.